Wear-Resistant Aluminum Bronze Alloy

Product Details
Customization: Available
Material: Cual
Transport Package: Plywood Case
Still deciding? Get samples of US$ 200/Piece
Request Sample
Gold Member Since 2020

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Registered Capital
73000000 RMB
Plant Area
>2000 square meters
  • Wear-Resistant Aluminum Bronze Alloy
  • Wear-Resistant Aluminum Bronze Alloy
  • Wear-Resistant Aluminum Bronze Alloy
  • Wear-Resistant Aluminum Bronze Alloy
  • Wear-Resistant Aluminum Bronze Alloy
  • Wear-Resistant Aluminum Bronze Alloy
Find Similar Products

Basic Info.

Trademark
WLVM
Origin
China
HS Code
8454909000

Product Description

The increase in the Al and Fe content results in a material in which the hard gamma 2 phase (about 400 HB) is present. By proper metallurgical control this hard constituent is uniformly distributed giving this alloy its ability to resist wear.
Mechanical and physical  Units
Nominal value
Tensile strength R m MPa  793
Specified non-proportional extension strength R p0.5 MPa  407

Elongation after breaking A
% 10

Brinell hardness
HBW 10/3000 228

Rockwell hardness
HRB 98

Reduction of area Z
% 8

Compressive strength R mc
Mpa 1069

Specified non-proportional compressive strength R pc0.1
Mpa 441

Compression ratio limit R pc
Mpa 338

Shear strength R cm
Mpa 427

Elastic modulus E
Gpa 110

Charpy shock absorption energy AK
J 11

Izod impact absorption power AK
J 16.3
Fatigue strength (100'000'000 times) σN Mpa 248

Density ρ
g / cm³ 7.45

Coefficient of linear expansion α
10-6 / K 16.2

Thermal conductivity λ
W / m · K 59

Conductivity γ
m /  Ω· mm² 7.5

Conductivity
% I.A.C.S. 13

Specific heat capacity cp
J / g · K 0.42

APPLICATIONS 
This product  is used for guide port bushings and wear strips replacing hardened steel and for some cams when no impact is involved. However, the largest single use is as die rings, inserts, forming rolls etc. in forming, bending or drawing operations, especially when stainless steel is the material being processed. This product is also widely used as work support blades for the centreless grinding of steel rods
Chemical composition
Al:10.5%   Fe:3.5%  Other:Up to 0.5%    The rest is copper
Wear-Resistant Aluminum Bronze Alloy
Wear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze AlloyWear-Resistant Aluminum Bronze Alloy
 

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier