Centrifugal Casting Cual

• Material: Cual
• Transport Package: Plywood Case
• Trademark: WLVM
• Origin: China
• HS Code: 8454909000

Product Description

This product is made by changing the heat treatment method of the alloy with special dual-phase structure and precise control of each production link. It has higher ultimate strength, yield strength and hardness

Mechanical and physical	Units	Nominal value
Tensile strength R m	MPa	793
Specified non-proportional extension strength R p0.5	MPa	407
Elongation after breaking A	%	10
Brinell hardness	HBW 10/3000	228
Rockwell hardness	HRB	98
Reduction of area Z	%	8
Compressive strength R mc	Mpa	1069
Specified non-proportional compressive strength R pc0.1	Mpa	441
Compression ratio limit R pc	Mpa	338
Shear strength R cm	Mpa	427
Elastic modulus E	Gpa	110
Charpy shock absorption energy AK	J	11
Izod impact absorption power AK	J	16.3
Fatigue strength (100'000'000 times) σN	Mpa	248
Density ρ	g / cm³	7.45
Coefficient of linear expansion α	10^-6 / K	16.2
Thermal conductivity λ	W / m · K	59
Conductivity γ	m /  Ω· mm²	7.5
Conductivity	% I.A.C.S.	13
Specific heat capacity cp	J / g · K	0.42

Application:
This product can meet the strict requirements of the aircraft industry. It has higher physical properties, hardness and sufficient ductility to withstand extreme shocks and loads. It is recommended to be used as bushes, bearing bushes, gaskets, inserts, piston parts, nuts and sliders.
Chemical composition
Al:10.5%   Fe:3.5%  Other:Up to 0.5%    The rest is copper