Characteristics: After vacuum melting and casting, the material composition is stable and uniform; The mature hot working and cold working technology combined with the heat treatment process makes the products have fine grains, uniform structure and good consistency of mechanical properties. High hardness, high conductivity and good thermal conductivity. Strong deformation resistance and high fatigue strength. No air hole, slag inclusion, sand hole and other defects, long service life.
Use of advantages: Improve casting and rolling speed, expand equipment capacity, aluminium strip billet bas fine grain.
The production process: Vacuum casting-Forgoing-Heart trestment-Machining.
Technical parameters: 1,CuCrZr:
Chemical compositions: Cr 0.3-1.2% Zr 0.08-0.3% Others Cu
Properties: HB≥130, Conductivity≥80%IACS
2,Low beryllium copper sleeve:
Chemical compositions: Ni 1.0-2.0% Be 0.1-0.3% Zr 0.1-0.3% Others Cu
Properties: δ≥65%IACS, HB≥200
3,High beryllium copper sleeve:
Chemical compositions: Be 1.8-2.0% Ni(Co) ≥0.2% Others Cu
Properties: HRC 36-45, Conductivity>261ACS
4,Diameter: Φ300-3000mm
Application area: Amorphous strip, Nd-Fe-B and other magnetic materials.